ABSTRACT FRACTURE BEHAVIOR OF BLOCK COPOLYMER AND GRAPHENE NANOPLATELET MODIFIED EPOXY AND FIBER REINFORCED/EPOXY POLYMER COMPOSITESByNicholas Thomas KamarGlass and carbon fiber reinforced/epoxy polymer composites (GFRPs and CFRPs) have high strength-to-weight and stiffness-to-weight ratios. Thus, GFRPs and CFRPs are used to lightweight aircraft, marine and ground vehicles to reduce transportation energy utilization and cost. However, GFRP and CFRP matrices have a low resistance to crack initiation and propagation; i.e. they have low fracture toughness. Current methods to increase fracture toughness of epoxy and corresponding GFRP and CFRPs often reduce composite mechanical and thermomechanical properties. With the advent of nanotechnology, new methods to improve the fracture toughness and impact properties of composites are now available. The goal of this research is to identify the fracture behavior and toughening mechanisms of nanoparticle modified epoxy, GFRPs and CFRPs utilizing the triblock copolymer poly(styrene)-block-poly(butadiene)-block-poly(methylmethacrylate) (SBM) and graphene nanoplatelets (GnPs) as toughening agents. The triblock copolymer SBM was used to toughen the diglycidyl ether of bisphenol-A (DGEBA) resin cured with m-phenylenediamine (mPDA) and corresponding AS4-12k CFRPs. SBM self assembled in epoxy to form nanostructured domains leading to larger increases in fracture toughness, KQ (MPa*m1/2) than the traditional, phase separating carboxyl-terminated butadiene-acrylonitrile (CTBN) rubber. Additionally, SBM increased the mode-I fracture toughness, GIc (J/m2) of CFRPs without corresponding reductions in composite three-point flexural properties and glass transition temperature (Tg). Fractography of SBM modified epoxy and CFRPs via scanning electron microscopy (SEM) showed that sub 100 nm spherical micelles cavitated to induce void growth and matrix shear yielding toughening mechanisms. Furthermore, SBM did not suppress epoxy Tg, while CTBN decreased Tg with both increasing concentration and acrylonitrile content. Graphene nanoplatelets (GnPs) consist of a few layers of graphene sheets, which are a single atomic layer of sp2 hybridized carbon atoms arranged in a honeycomb lattice. GnPs have excellent thermal, electrical and mechanical properties and are thus attractive fillers for composite materials.GnPs with a basal plane diameter of 5 μm were incorporated between lamina in GFRPs made via vacuum assisted resin transfer molding (VARTM). At only 0.25 wt%, GnPs improved GFRP flexural strength and GIc by 29 and 25%, respectively. GnPs also improved the low velocity drop weight impact properties of the GFRP laminates. Ultrasonic C-scans and dye penetration experiments on impacted laminates showed that the impact-side damage area decreased with increasing concentration of GnPs, while the back-side damage area increased. The addition of GnPs improved absorption and dissipation of impact energy throughout GFRP laminates. Additionally, GnPs were investigated as toughening agents in epoxy and corresponding AS4-12k CFRPs. In epoxy and CFRPs, GnPs activate a crack deflection toughening mechanism, resulting in increased fracture surface area and fracture energy. Hybrid GnP/SBM modified epoxy and CFRPs were also investigated.
Read
